Product Description:
PE A4009MFN1325 is a high-density polyethylene homopolymer with a narrow molecular weight distribution primarily intended for the extrusion of monofilaments.
A4009MFN1325 CHARACTERISTICS:
- High tenacity monofilaments & tapes
- Very low gels content
- Superior processability & surface quality
- Very low MVTR (Moisture Vapour Transmission Rate)
Examples of applications:
- Extrusion of monofilaments
- High tenacity tapes
- Cereal liners film
- Injection moulding
- Blow-moulding for food packaging
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| Melt flow rate, (2.16 kg), g/10min | 0.7 – 1.1 | g/10 min | ISO 1133 Cond. D |
| Density | 0.958-0.962 | Kg/m³ | ISO 1183/A |
| Flexural Modulus (1% secant), @ 1.4 mm/min | 1000 – 1100 | MPa | ISO 178 |
| Tensile Strength @ Yield at 50 mm/min | 27 – 30 | MPa | ISO 527‐2 |
| Tensile Strength @ Break at 50 mm/min | 19 – 22 | % | ISO 527‐2 |
| Elongation at break | > 500 | % | ISO 527‐2 |