Classification:
- General purpose
- High Impact Strength
Characteristic:
- Medium Impact Resistance
- Medium Flow
Application:
- Electronic and Electrical parts
- vacuum cleaners
- washing machine covers
- Refrigerator door caps
DRYING:
It is recommended that ABS Resins be dried at (80-85°c) for 3 hours.
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| Izod impact (6.4 mm, notched) | 23 | Kj/m2 | D-256 |
| Melt flow index (220°C, 10 kg) | 35 | gr/10 min | D-1238 |
| Rock well hardness | 109 | R-scale | D-785 |
| HDT (1.82 m pa) | 85 | °C | D-648 |
| Vicat softening Temp (5kg/50°C) | 95 | °C | D-1525 |
| Tensile strength (23°C, 50 mm/min) | 455 | Kg/cm2 | D-638 |
| Tensile elongation (23°C, 50 mm/min) | 20 | % | D-638 |
| Flexural strength (23°C, 2.8 mm/min) | 650 | Kg/cm2 | D-790 |
| Flexural Modulus (23°C, 2.8 mm/min) | 20000 | Kg/cm2 | D-790 |
| Specific Gravitv (23°C) | 1.04 | …… | D-792 |
| Molding Shrinkage | 0.4-0.7 | % | D-955 |
| Flammability (1/8inch(3.2mm)) | HB | …… | U194 |