Classification:
- Extrusion
- Medium Impact Strength
Characteristic:
- Super High Impact Resistance
Application:
- Automobile parts (radiator grill &etc.)
- Helmets
- Toys
- Suitcases
- Profiles Released extruded product
- Bobbin sleeves
- Boats
- pipes
- bath tubs
DRYING:
It is recommended that ABS Resins be dried at (80-85°c) for 3 hours.
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| Izod impact (6.4 mm, notched) | 26 | Kj/m2 | D-256 |
| Melt flow index (220°C, 10 kg) | 14 | gr/10 min | D-1238 |
| Rock well hardness | 113 | R-scale | D-785 |
| HDT (1.82 m pa) | 90 | °C | D-648 |
| Vicat softening Temp (5kg/50°c) | 100 | °C | D-1525 |
| Tensile strength (23°C, 50 mm/min) | 470 | kg/cm2 | D-638 |
| Tensile elongation (23°C, 50 mm/min) | 25 | % | D-638 |
| Flexural strength (23°c, 2.8 mm/min) | 670 | Kg/cm2 | D-790 |
| Flexural Modulus (23°C, 2.8 mm/min) | 22000 | Kg/cm2 | D-790 |
| Specific Gravity (23°C) | 1.04 | ……. | D-792 |
| Molding Shrinkage | 0.4-0.7 | % | D-955 |
| Flammability (1/8inch(3.2mm)) | HB | ……. | U194 |