Product Description:
- General purpose
- Sheet
- Extrusion grade
Features:
- Sheet Grade
- Extrusion grade
- High rigidity& high impact strength
Application:
- Refrigerator interior container and door liner (cyclopen-tane Blowing agent use) and etc
DRYING:
It is recommended that ABS Resins be dried at (80-85°c) for 3 hours. Extruder with one-stage or two-stage venting are recommended for extrusion of sheet compression
| PROPERTY | VALUE | UNIT | TEST METHOD |
|---|---|---|---|
| Izod impact (6.4 mm, notched) | Min 33 | Kj/m2 | D-256 |
| Melt flow index (220°C, 10 kg) | 4-10 | gr/10 min | D-1238 |
| Rock well hardness | 95-110 | R-scale | D-785 |
| HDT (1.82 m pa) | Min 85 | •C | D-648 |
| Vicat softening Temp (5kg/50°C) | Min 94 | °C | D-1525 |
| Tensile strength (23°C, 50 mm/min) | Min 440 | Kg/cm2 | D-638 |
| Tensile elongation (23°C, 50 mm/min) | Min 25 | % | D-638 |
| Flexural strength (23°C, 2.8 mm/min) | Min 640 | Kg/cm2 | D-790 |
| Flexural Modulus (23°C, 2.8 mm/min) | Min 20000 | Kg/cm2 | D-790 |
| Specific Gravity (23 °C) | 1.04 | ……. | D-792 |
| Molding Shrinkage | 0.4-0.7 | % | D-955 |
| Flammability (1/8inch (3.2mm) ) | HD | ……. | U194 |